Application recommendations
Inserts, cutting data recommendations
The cutting data recommendations in the table are guide values
and depend to a high degree on the stability of the machine, xture and workpiece.
Cutting groups Material group Composition / structure Tensile Hard- Cutting speed vc m/min Feed rate fz mm/z
strength ness
RM HB PCD / PCD 1
(MPa) HRC
K10 G12 G16 G26 PCD 3 PCBN W 3108-…. W 6120-….
PCD C
1.1 C = 0.1 -0.25 annealed, long cutt. 420 125 240-280 190-330 0.05-0.15 0.05-0.25
1.2 420 125
2.1 Unalloyed steel C = 0.1 -0.25 annealed, short-chip 620 190 240-280 190-330
2.2 Cast steel 640 190
3 Machining steel C = 0.25 -0.55 annealed,long cutt. 850 250 220-260 180-220
4 915 270
5 C = 0.25 -0.55 annealed,short-chip 1020 300 220-260 180-220
6 610 180
C = 0.25 -0.55 tempered 210-250 170-210
Low-alloy steel
7 C = 0.25 -0.8 annealed 200-240 160-200
Cast steel C = 0.25 -0.8 tempered 190-230 150-190
8 Machining steel
9 annealed 140-180 110-150
High-alloy steel tempered 930 275 130-170 100-140
10
tempered 1020 300 130-170 100-140
Cast steel tempered 1190 350 130-170 100-140
High-alloy
11 annealed 680 200 100-140 90-130
tool steel
Stainless steel hardened and tempered 1100 325 110-150 90-120
12-13
and cast steel ferritic/martensitic annealed 680 200 100-140 80-120
14.1 810 240 100-140 80-120
Stainless steel martensitic 610 180 100-140 80-120
14.2 880 260 90-130 70-110
15 austenitic quenched 180 90-130 170-250
Grey cast iron 90 260 80-120 140-180 90-130
16 austenitic/ferritic (duplex) 100 160 70-110 130-170
17 Cast iron with 250 60-90 100-140 90-130
18 nodular cast iron perlitic/ferritic 400 130 80-120 140-180 600-800
19 1050 230 60-90 120-160 400-600
Malleable perlitic (martensitic) 60 -1000 -1500 400-600
20 100 -800 -1200
21 Aluminium ferritic 75 -800 -1200 500-800
22 forging alloys 90 -600 -1000
23 perlitic 130 -800 -5000
Aluminium 110 200-300 350-450 -5000
24 ferritic 90 200-300 350-450 -5000
casting alloys 100 200-300 350-550 -5000
25 perlitic -1500
26 Copper 240-280 400-500 -2000
27 Copper alloys not heat treatable 240-280 400-500 -2000
28 (bronze, brass) 200 40-60 -2000
29 Non metallic heat treatable/heat treated 230 40-60 -3000
30 materials 250 40-60 -3000
31 <12% Si not heat treatable 350 35-55
32 320 35-55 150-300
Heat resistant <12% Si heat treatable/heat treated
33 35-55
alloys >12% Si not heat treatable 50-70
34
35 Machined alloys, Pb >1%
36
Titanium alloys CuZn, CuSnZn
37
38 Cu lead free Copper/elektrolyte copper
Hardened steel
39 Duroplastic
Reinforced materials
Fe-based annealed
heat treated
Ni- or Co-based annealed
heat treated
cast
pure titanium
Alpha-beta alloys
50-62
39